ASTM A105 Round Bar
| Specifications | ASTM B446 / ASTM SB446 |
| size | 2-100mm A/F |
|---|---|
| Square bar size | 4 to 100mm |
| Flat bar size | Thickness: 2 -100mm Width: 10 to 500mm |
| Round bar size | Diameter: 3-~800mm |
| Rectangles Size | 33 x 30mm to 295 x 1066mm |
| Angle bar size | 3mm*20mm*20mm~12mm*100mm*100mm |
| Section | 3.0 to 12.0mm thickness |
| Channel Bar | 80 x 40mm to 150 x 75mm section; 5.0 to 6.0mm thickness |
| Hollow Bar | 32mm OD x 16mm ID to 250mm OD x 200mm ID) |
| Billet Size | 1/2" to 495mm Diameter |
| Finish | Cold (bright) drawn, centreless ground, hot rolled, smooth turned, peeled, slit rolled edge, hot rolled annealed, Rough Turned, Bright, Polish, Grinding, Centreless Ground & Black |
| Tolerance | H8, H9, H10, H11, H12, H13K9, K10, K11, K12 or as per clients’ requirements |
| Surface | Hot Rolled Pickled, Bright, Sand Blasting Finished, Cold Drawn, Hairline, Polished |
| Condition | Hardened & tempered, annealed |
| Technique | Cold Drawn, Hot Rolled, Forged Round Bar,Cold Rolled, Rod |
| Processing | Bar cutting to 650mm |
| Form | Round, Welding Rod, T-Bar, Rod, Precision Ground Bar, Channel Bar, Square, Flat Bar, Blocks, Round Rod, Hollow, Rings, Rectangle, Hex (A/F), Triangle, Threaded, Profiles, Billet, Ingot, I/H Bar, Half Round Bar, Forging etc. |
| Metric | US Bar | ASTM/ Canadian | Japanese | ||||
|---|---|---|---|---|---|---|---|
| Bar Size | Diam. (mm) | Bar Size | Diam. (Inch) | Bar Size | Diam. (mm2) | Bar Size | Diam. (mm) |
| 5 | 5 | #2 | 0.250 | 10M | 100 | 6 | 6 |
| 5.5 | 5.5 | #3 | 0.375 | 15M | 200 | 10 | 10 |
| 6 | 6 | #4 | 0.500 | 20M | 300 | 13 | 13 |
| 7 | 7 | #5 | 0.600 | 25M | 500 | 16 | 16 |
| 8 | 8 | #6 | 0.750 | 30M | 700 | 19 | 19 |
| 9 | 9 | #7 | 0.875 | 35M | 1000 | 22 | 22 |
| 10 | 10 | #8 | 1.000 | 45M | 1500 | 25 | 25 |
| 11 | 11 | #9 | 1.125 | 55M | 2500 | 29 | 29 |
| 12 | 12 | #10 | 1.250 | 32 | 32 | ||
| 14 | 14 | #11 | 1.375 | 35 | 35 | ||
| 16 | 16 | #12 | 1.500 | 38 | 38 | ||
| 18 | 18 | #13 | 1.600 | 41 | 41 | ||
| 20 | 20 | #14 | 1.750 | 44 | 44 | ||
| 22 | 22 | #15 | 1.875 | 48 | 48 | ||
| 25 | 25 | #16 | 2.000 | 51 | 51 | ||
| 28 | 28 | #18 | 2.250 | 57 | 57 | ||
| 32 | 32 | ||||||
| 36 | 36 | ||||||
| 40 | 40 | ||||||
| 44 | 44 | ||||||
| 50 | 50 | ||||||
|
ELEMENT
|
COMPOSITION, %
|
|
Carbon
|
0.35 max
|
|
Manganese
|
0.60-1.05
|
|
Phosphorus
|
0.035 max
|
|
Sulfur
|
0.040 max
|
|
Silicon
|
0.10-0.35
|
|
Copper
|
0.40 max (1)
|
|
Nickel
|
0.40 max (1)
|
|
Chromium
|
0.30 max (1-2)
|
|
Molybdenum
|
0.12 max (1-2)
|
|
Vanadium
|
0.08 max
|
|
Mechanical Properties
|
Requirements
|
|---|---|
|
Tensile strength,min,psi [MPa]
|
70000 [485]
|
|
Yield strength,min,psi [MPa]
|
36000 [250]
|
|
Elongation, min, %
|
30
|
|
Reductionofarea,min,%
|
30
|
|
Hardness,HB,max
|
187
|
|
Density (lb / cu. in.)
|
0.284
|
|
Specific Gravity
|
7.9
|
|
Specific Heat (Btu/lb/Deg F – [32-212 Deg F])
|
0.107
|
|
Melting Point (Deg F)
|
2740
|
|
Thermal Conductivity
|
360
|
|
Mean Coeff Thermal Expansion
|
6.7
|
|
Modulus of Elasticity Tension
|
30
|
|
Modulus of Elasticity Torsion
|
11
|
Taiwan, Egypt, Australia, Lithuania, Israel, Vietnam, Gabon, Croatia, Hong Kong, Estonia, United Arab Emirates, Nigeria, Bolivia, Netherlands, Iraq, United Kingdom, Sweden, China, Bahrain, Pakistan, Sri Lanka, United States, Malaysia, South Africa, Oman, Serbia, Spain, Greece, South Korea, Denmark, Italy, Russia, Algeria, Colombia, Azerbaijan, Iran, Mongolia, Belgium, Iran, Ukraine, Nigeria, Venezuela, Afghanistan, Switzerland, Kazakhstan, Jordan, Trinidad & Tobago, Poland, Morocco, Mexico, Belarus, France, Peru, Philippines, New Zealand, Saudi Arabia, Tunisia, Yemen, Czech Republic, Finland, Libya, Slovakia, Singapore, Hungary, Kenya, Japan, Chile, Costa Rica, Norway, Qatar, Ghana, Austria, Bhutan, Indonesia, Bangladesh, Mexico, Bulgaria, Canada, Thailand, Kuwait, Poland, Angola, Turkey, Chile, Lebanon, Brazil, Portugal, Argentina, Ecuador, Romania